CoolPoly® D5108
聚苯硫醚
Cool Polymers, Inc.
Technical Data
产品说明
CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties.
总体
材料状态 • 已商用：当前有效
资料 1 • Processing (English)
• Technical Datasheet (English)
UL 黄卡 2 • E229777-101082284
• E229777-538500
搜索 UL 黄卡 • Cool Polymers, Inc.
• CoolPoly®
供货地区 • 北美洲 • 欧洲
• 南美洲 • 亚太地区
性能特点 • 导热 • 绝缘 • 良好的成型性能
形式 • 颗粒料
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
密度 1.82g/cm³ ISO 1183
收缩率 ASTM D955
流动 0.20%
横向流动 0.40%
机械性能 额定值单位制 测试方法
拉伸模量 23600MPa ISO 527-2
拉伸应力 (屈服) 37.0MPa ISO 527-2
断张率 0.16% ISO 527-2
弯曲模量 19400MPa ISO 178
弯曲强度 69.0MPa ISO 178
冲击性能 额定值单位制 测试方法
简支梁缺口冲击强度 1.1kJ/m² ISO 179
简支梁缺口冲击强度 2.5kJ/m² ISO 179
热性能 额定值单位制 测试方法
热变形温度
0.45 MPa, 未退火 276°C ISO 75-2/B
1.8 MPa, 未退火 239°C ISO 75-2/A
线形膨胀系数 ISO 11359-2
流动 6.5E-6cm/cm/°C
横向 5.0E-6cm/cm/°C
导热系数 10W/m/K ASTM C177
电气性能 额定值单位制 测试方法
表面电阻率 4.5E+14ohm ASTM D257
体积电阻率 2.5E+16ohm•cm ASTM D257
介电强度 29kV/mm ASTM D149
介电常数 ASTM D150
100 Hz 4.80
1 MHz 3.70
耗散因数 ASTM D150
100 Hz 0.022
1 MHz 0.0023
耐电弧性 300sec ASTM D495
CoolPoly® D5108
聚苯硫醚
Cool Polymers, Inc.
电气性能 额定值单位制 测试方法
相比耐漏电起痕指数(CTI) 580V UL 746
热丝引燃 (HWI) 120sec UL 746
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.00 mm) V-0 UL 94
补充信息
The value listed as Nominal Tensile Strain at Break, ISO 527-1, -2, was tested in accordance with ASTM D412.
The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM E1461.
The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with ASTM D551.
The value listed as Specific Heat ASTM C351, was tested in accordance with ASTM E1461.
Thermal Diffusivity, ASTM E1461: 0.07 cm²/sec
Comparative Tracking Index, ASTM 3638: 580 volts
Hot Wire Ignition, ASTM D3874: >120 sec
High Voltage Arc Tracking Rate, UL-746A: did not track
High Voltage Arc Resistance to Ignition, UL-746A: >300 sec
注射 额定值单位制
干燥温度 150°C
干燥时间 6.0hr
Dew Point -40.0°C
建议的最大水分含量 0.0%
螺筒后部温度 290 到 315°C
螺筒中部温度 300 到 320°C
螺筒前部温度 310 到 340°C
射嘴温度 316 到 340°C
加工（熔体）温度 307 到 338°C
模具温度 135 到 177°C
注塑温度 60.0 到 165MPa
注射速度 中等偏快
保压 40.0 到 105MPa
背压 0.200 到 0.500MPa
螺杆转速 75 到 180rpm
垫层 5.00 到 13.0mm
螺杆压缩比 2.5:1.0