VICTREX® PEEK 150GL30 BLACK

 

Polyetheretherketone

 

Victrex plc

 

Technical Data

 

Product Description

 

High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black.

 

Complex geometries with thin cross sections or long flow lengths where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.

 

General

 

Material Status • Commercial: Active

 

• Brochure - Chemical Resistance (English) 

• Processing - Victrex PEEK Compression Molding Guide (English) 

Literature 1 • Processing - Victrex PEEK Extrusion Guide (English)

Processing - Victrex PEEK Finishing Operations (English)

•

• Processing - Victrex PEEK Injection Molding Guide (English)

• Technical Datasheet (English)

UL Yellow Card 2 • E161131-224302

E161131-531779

•

Search for UL Yellow Card • Victrex plc

• VICTREX® PEEK

Availability • Asia Pacific • Europe • North America

Filler / Reinforcement • Glass Fiber, 30% Filler by Weight

Features • Food Contact Acceptable • Good Flow • High Strength

• Good Chemical Resistance • Good Sterilizability • Semi Crystalline

Uses • Medical/Healthcare • Non-specific Food Applications

Applications

Agency Ratings • FDA Food Contact, Unspecified Rating

Appearance • Black

Forms • Granules

Processing Method • Injection Molding

Physical Nominal Value (English) Nominal Value (SI) Test Method

Density 4 1.52 g/cm³ 1.52 g/cm³ ISO 1183

Spiral Flow 5 5.91 in 15.0 cm Internal Method

Molding Shrinkage 6 ISO 294-4

Across Flow : 356°F (180°C) 0.90 % 0.90 %

Flow : 356°F (180°C) 0.30 % 0.30 %

Water Absorption ISO 62

73°F (23°C), 24 hr, 0.126 in (3.20 mm) 0.040 % 0.040 %

Equilibrium, 73°F (23°C), 0.126 in (3.20 mm), 0.30 % 0.30 %

50% RH

Mechanical Nominal Value (English) Nominal Value (SI) Test Method

Tensile Modulus (73°F (23°C)) 1.74E+6 psi 12000 MPa ISO 527-2

Tensile Stress ISO 527-2

Break, 73°F (23°C) 27600 psi 190 MPa

Break, 257°F (125°C) 16700 psi 115 MPa

Break, 347°F (175°C) 10200 psi 70.0 MPa

Break, 437°F (225°C) 7980 psi 55.0 MPa

Break, 527°F (275°C) 5800 psi 40.0 MPa

Tensile Strain (Break, 73°F (23°C)) 2.4 % 2.4 % ISO 527-2

Flexural Modulus (73°F (23°C)) 1.67E+6 psi 11500 MPa ISO 178

Flexural Stress (73°F (23°C)) 39200 psi 270 MPa ISO 178

 

VICTREX® PEEK 150GL30 BLACK

 

Polyetheretherketone

 

Victrex plc

Mechanical Nominal Value (English) Nominal Value (SI) Test Method

Compressive Stress ISO 604

73°F (23°C) 36300 psi 250 MPa

248°F (120°C) 23200 psi 160 MPa

392°F (200°C) 7980 psi 55.0 MPa

Impact Nominal Value (English) Nominal Value (SI) Test Method

Notched Izod Impact Strength (73°F (23°C)) 3.6 ft•lb/in² 7.5 kJ/m² ISO 180/A

Unnotched Izod Impact Strength (73°F (23°C)) 24 ft•lb/in² 50 kJ/m² ISO 180

Hardness Nominal Value (English) Nominal Value (SI) Test Method

Shore Hardness (Shore D, 73°F (23°C)) 87 87 ISO 868

Thermal Nominal Value (English) Nominal Value (SI) Test Method

Heat Deflection Temperature ISO 75-2/A

264 psi (1.8 MPa), Unannealed 635 °F 335 °C

Glass Transition Temperature 289 °F 143 °C ISO 11357-2

Melting Temperature 649 °F 343 °C ISO 11357-3

CLTE ISO 11359-2

Flow : > 289°F (> 143°C) 1.1E-5 in/in/°F 2.0E-5 cm/cm/°C

Flow : < 289°F (< 143°C) 1.1E-5 in/in/°F 2.0E-5 cm/cm/°C

Transverse : < 289°F (< 143°C) 2.5E-5 in/in/°F 4.5E-5 cm/cm/°C

Transverse : > 289°F (> 143°C) 6.1E-5 in/in/°F 1.1E-4 cm/cm/°C

Specific Heat (73°F (23°C)) 0.406 Btu/lb/°F 1700 J/kg/°C DSC

Thermal Conductivity (73°F (23°C)) 2.1 Btu•in/hr/ft²/°F 0.30 W/m/K ISO 22007-4

RTI Elec 464 °F 240 °C UL 746

RTI Imp 428 °F 220 °C UL 746

RTI Str 464 °F 240 °C UL 746

Electrical Nominal Value (English) Nominal Value (SI) Test Method

Volume Resistivity 5.0E+15 ohms•cm 5.0E+15 ohms•cm IEC 60093

Electric Strength (0.0787 in (2.00 mm)) 550 V/mil 22 kV/mm IEC 60243-1

Dielectric Constant (73°F (23°C), 1 kHz) 3.40 3.40 IEC 60250

Comparative Tracking Index 150 V 150 V IEC 60112

Flammability Nominal Value (English) Nominal Value (SI) Test Method

Glow Wire Flammability Index IEC 60695-2-12

0.0787 in (2.00 mm) 1760 °F 960 °C

Fill Analysis Nominal Value (English) Nominal Value (SI) Test Method

Melt Viscosity (752°F (400°C)) 290 Pa•s 290 Pa•s ISO 11443

Injection Nominal Value (English) Nominal Value (SI)

Drying Temperature 248 to 302 °F 120 to 150 °C

Drying Time 3.0 to 5.0 hr 3.0 to 5.0 hr

Hopper Temperature < 212 °F < 100 °C

Rear Temperature 680 °F 360 °C

Middle Temperature 689 to 698 °F 365 to 370 °C

Front Temperature 707 °F 375 °C

Nozzle Temperature 716 °F 380 °C

Mold Temperature 338 to 392 °F 170 to 200 °C

Injection Notes

Runner: Die / nozzle >3mm, manifold >3.5mm

 

Gate: >2mm or 0.5 x part thickness

 

 

 

 

 

 